Composite electrode for consumable electrode arc welding process

ABSTRACT

A consumable composite electrode of infinite length for use in an automatic arc-welding of steel without shielding gas and the like shielding means comprising a steel sheath and a powdery mixture filled within the sheath and having a specific composition which contributes to the arc-welding of the steel workpiece.

- [52] US. Cl

United States Patent on 3,560,702

[72] Inventors Masayasu Arikawa; [51] Int. Cl 823k 35/22 Motomi Kano, F ujisawa-shi: Sho Horiuchi. [50] Field of Search 219/146;

Kamakura-shi, Japan [21] Appl No 801,690

[22] Filed Feb. 24, 1969 [45] Patented Feb. 2, 1971 [73] Assignee Kobe Steel Ltd.

Hyogo-ken. Japan a corporation of Japan [32] Priority Mar. 2, 1968 [33] Japan [54] COMPOSITE ELECTRODE FOR CONSUMABLE ELECTRODE ARC WELDING PROCESS 6 Claims, 2 Drawing Figs.

[ 5 6] References Cited UNITED STATES PATENTS 3.424.892 l/l969 Wilcox 219/146 Primary Examiner.l. V. Truhe Assistant Examiner-Lawrence A. Rouse Attorney-Wenderoth, Lind and Ponack ABSTRACT: A consumable composite electrode of infinite length for use in an automatic arc-welding of steel without shielding gas and the like shielding means comprising a steel sheath and a powdery mixture filled within the sheath and having a specific composition which contributes to the arc-welding of the steel workpiece.

N2 IN THE WELDED STEEL (wi/o) KCL+NOCL IN AL-Mg ALLOY (wl PATENTED FEB 2m:

0.006 006 KCLfN OCL IN AL-Mg ALLOY (wt /0) 30% 6M5 Sod; ME 7: Z

1x. :3 PZmFZOU MEDPQOE 0006 KCL+NOCL 1N AL-Mg ALLOY (wr/o) MASAYASU ARIKAWA, INVENTOR S MOTOMI KANO AND SHO HORIUCHI evwmwmmmml ATTORNEYS COMPOSITE ELECTRODE FOR CONSUMABLE ELECTRODE ARC WELDING PROCESS BACKGROUND OF THE INVENTION For automatically welding a workpiece such as steel, the socalled gas-shielded arc-welding process in which carbonic acid gas or an inert gas or a mixture thereof is employed as the arc shielding means and the so-called submerged arc-welding process in which a specific flux is employed as the arc shielding means have been known as most practical welding processes. In addition, the so-called electroslag welding process has been also known. These processes are common to each other in the fact that in any of the above-mentioned known automatic welding processes a coiled steel wire of infinite length has been employed as the consumable electrode and the electrode is melted under conditions which shield the electrode from the atmosphere whereby the molten metal from the consumable electrode is transferred to the workpiece to be welded to deposit a metal thereon.

Furthermore, of late, several types of consumable electrode welding processes which do not require any external shielding gas supply source have been proposed and practically em ployed.

However, the efficiency of any of the above-mentioned known welding processes which necessarily employ a shielding gas is adversely affectedby even wind which is blowing'at and in the vicinity of the welding zone where the arc is being struck at the velocity on the order of 2m/sec. and a satisfactory weld can not be obtained. This difficulty has been oneof most serious drawbacks common to the above-mentioned known welding processes. And according to the submerged arc welding process wherein a welding operation is carried out while supplying a particular flux into the groove or recess provided in the workpiece, the are being struck can not be externally observed and the welding position is subjected to limitation and therefore, the submerged arc welding process can not be applied to certain locations.

More recently, a consumable electrode welding process which does not require any external shielding gas supply source has been proposed. However, welds formed by such a process very often have too low impact values to make them practically useful. Thus, development of more useful and improved consumable electrodes which do not require shielding gas have been eagerly called for by the art.

One typical arc-welding process which does not require the use of any shielding gas and can be carried out in the open air has been disclosed in U.S. Pat. No. 2,909,778.

The welding process of this U. S. Patent is characterized in that a welding are being struck is supplied with a killing agent which acts on the molten metal from a consumable electrode and with a killing agent protector which shields the killing agent from oxygen and nitrogen in the air. For use in such a welding process an electrode which comprises a metal the interior of which is filled with a deoxidizer, the killing agent and killing agent protector has been proposed. As the deoxidizer to be employed in such a wire, one or more members selected from the group comprising Mn, Cr, Nb, Ta and V are selectively employed, as the killing agent to be employed in the wire, one or more members selected from the group comprising Zr, Ti, B, Al, Si, Li and Ca are selectively employed and as the killing agent protector to be employed in the wire, one or more members selected from the group comprising aluminum fluoride and halides of alkali or alkaline earch metal are selectively employed. Although the use of the last-mentioned composite wire electrode may form a less porosity deposit metal, the deposit metal often contains a substantial amount of killing agent residue.

When the deposit metal contains a substantial amount of killing agent such as Al, Ti and/or Zr, although these elements can bond with nitrogen as well as oxygen, once AlN, TiN and/or ZrN which have high specific gravities and high melting points have been formed in a welding puddle, the possibility of slagging off for these elements is very rare and they remain in the deposit metal as nonmetal intervenient substances which tend to reduce the ductility of the deposit metal. Therefore, when a deposit metal contains the killing agent such as Ti, Zr, Al, B and/or the like enumerated hereinabove in a substantial amount, the metal has a very low impact value which renders the metal unsuitable for use in constructions which among others require varying high resistances against impact. This is one of the most important reasons for which commercially available conventional welding electrodes have been used to only limited applications.

Another example of arc-welding process which does not require any shielding gas or, if any, requires only a small amount of shielding gas has been disclosed in U. S. Pat. No. 3,1 18,053. The electrode employed in the welding process of this U.S. patent comprises a composite wire which consists of a metal sheath the interior of which is filled with a welding flux wherein carbonate of lime is present as a gas evolution agent.

As the composite wire is melted, the carbonate of lime is pyrolyzed to evolute gas which is to be used as the shielding gas.

However, in such an arc welding process using the composite wire electrode containing the gas evolution agent, since the reaction takes place rapidly in the are being struck, the arc is disturbed under the influence of the evolving gas and rather increases the amount of nitrogen in the deposit metal.

Furthermore, when the deoxidizer and denitrification agent such as Al, Zr and etc. are used in combination with a carbonate, the C contained in the carbonate is reduced and a portion of the C is liable to be transferred to the deposit metal resulting in reduction of the impact value of the deposit metal.

SUMMARY OF THE INVENTION One primary object of the present invention is to provide an improved consumable composite electrode for use in an arcwelding of steel which enables the welding process to be carried out in the open air without the use of any shielding gas and which makes it possible to obtain a high quality deposit metal.

Another object of the present invention is to provide an improved consumable composite electrode for use in an arcwelding process of steel which can effectively eliminate the above-mentioned defects inherent to the conventional opentype arc-welding processes.

A still further object of the present invention is to provide an improved consumable composite electrode for use in an arc-welding process which enables the welding process to be carried out in the open air without the use of any shielding gas and which makes it possible to obtain a high quality deposit metal which has excellent X-ray and mechanical properties and especially, a high impact value.

A further object of the present invention is to provide an improved high weldability electrode for use in an arc-welding of steel which enables the welding process to be carried out in the open air with the use of either DC or AC power source.

According to one aspect of the present invention, there is provided a consumable composite electrode which comprises a metal sheath and a powdery flux filled in the interior of the sheath and essentially comprising by weight of the total wire electrode, respectively, 6-11 percent of CaF 0.ll.5 percent of Mn, 0.8-2 percent of Ni and 2-5 percent of Al-Mg alloy containing the total amount of 0.0060.06 percent of Na and K in the form of chlorides.

In carrying out an arc-welding of steel with the use of the consumable composite electrode according to the present invention, the electrode is continuously fed toward and along the groove or recess provided in the steel workpiece by a suitable feeding means and cooperates with an arc to be struck between the electrode and workpiece in forming a deposit metal in the groove by transferring the molten metal of the electrode to the groove. When the electrode is fed and melted in the manner mentioned above, the ingredients of the flux filled in the interior of the metal sheath of the electrode acts as follows. That is, the CaF forms slag which serves as means for enveloping and shaping a welding bead, the Mn serves as the deoxidizer and is added to the deposit metal as one of the alloying elements of the deposit metal, the Ni serves as the socalled austenite former and finally, the Al-Mg alloy effectively serves as the denitrification agent. Thus, these flux ingredients in combination provide a high quality deposit metal under satisfactory welding conditions.

The reason for which Al-Mg alloy is used as the deoxidizer in the novel wire electrode is that when Al and Mg are employed in the form of simple substances in the wire, a substantially amount of spattering will take place which renders the welding process impractical. This is due to the fact that Joule 's heat which is generated in the gap between the conductive tip end of the wire and the arcing spot by the current flowing through C. the wire rapidly heats the wire end before the wire end reaches the arcing spot, but in such a case the Mg of the flux is rapidly oxidized to the explosion point. On the contrary, when Al and Mg are contained in the flux in the form of Al-Mg alloy, such a phenomenon will not take place and the conditions of the arc may be substantially improved which enables the welding operation to be conducted with the use of a AC power source. Furthermore, the use of Al-Mg alloy as the deoxidizer in the flux of the novel wire electrode rather than Al and Mg in the form of simple substances reduces the melting point of these ingredients thereby to enhance the deoxidization and denitrification actions of these ingredients. If Mg in the form of simple substance is incorporated in the flux of the wire electrode as the deoxidizer, when the wire is backed at the temperature 380- 400 C. in the final step in the production of the wire the oxidization of the Mg is accelerated and the thus produced wire can not have desired properties which are called for such a wire. From the above reason, according to the present invention Al and Mg are employed in the form of Al-Mg alloy. In the novel consumable composite wire electrode the blending ratio of Al to Mg is preferably one to one and when expressed by the term of weight percent of the total Al-Mg alloy, the ratio useful in the present invention may be as follows:

Al 35-65 weight percent Ag 65-35 weight percent Any ratio which deviates from the above-mentioned ratio range will produce substantially the same defects as those described in connection of the use of Mg in its simple substance form and is out of the scope of the present invention.

Furthermore, according to the present invention, the powdery denitrification agent comprises as its essential ingredient the specific Al-Mg alloy, that is, the Al-Mg alloy including NaCl and KCl and the amount of the total of NaCl and KCI is of 0.0060.06 percent by weight of the Al-Mg alloy. The effects and advantages obtainable by the use of such a specific denitrification agent in the flux of the novel wire electrode will be in detail described hereinbelow referring to the accompanying drawing.

BRIEF DESCRIPTION OF THE DRAWING FIG. I is a graph showing the relationship between the amount of KCl and NaCl in the Al-Mg alloy used in the novel wire electrode and that of N to be contained in a deposit metal fonned by an arc-welding position using the wire electrode; and

FIG. 2 is a graph showing the relationship between the amount of KCl and NaCl in the Al-Mg alloy used in the novel wire electrode and that of the moisture content to be absorbed in a deposit metal obtained by an arc-welding operation using the wire electrode.

DETAILED DESCRIPTION In order to detennine the relationship between the amount of KCl and NaCl contained in the Al-Mg alloy in the flux used in the novel wire electrode and that of N to be contained in a deposit metal, an open-arc automatic welding operation was conducted using a composite wire electrode in the metal sheath of which 20 percent of powdery flux by weight of the total wire electrode was filled and the powdery flux had the following composition:

BY WEIGHT OF THE TOTAL WIRE ELECTRODE CaF 8% AlF 1% MaF 1% Fe-Mr 0.6% percent Mn) Si0 0.6%

Iron powder 3.4%

Al-Mg alloy 3.2%

CaCO 0.8%

The result of the welding operation is shown in FIG. 1 and as seen from this FIG., as the amount of KC 1 NaCl increases the amount of N to be contained in a deposit metal decreases accordingly. This is supposedly due to the fact that when Al- Mg alloy containing K and Na is used in the flux of the wire electrode, the Mg which has been exposed to the are is vaporized at the boiling point of 1070 C and coexists with K and Na which serve as ionization agents in the flux thereby to exhibits a strong arc stabilization action and that since the arc is not disturbed and transfer of the molten metal drops at the tip end of the wire electrode to the workpiece can be smoothly realized, the time during which the molten metal drops are exposed to the air will be shortened resulting in decrease of the amount of N to be absorbed into a deposit metal to be formed.

In this way, with the use of the novel consumable composite wire electrode a satisfactory atmosphere shielding effect can be expected for. Therefore, the amount of denitrification powders which are to be blended with the other ingredients of the flux of the wire for the purpose of prevention of formation of air voids in a deposit metal can be reduced without the use of an auxiliary agent such as carbonate and the like whereby adverse effects on the mechanical properties of the deposit metal which will be otherwise inevitable can be effectively prevented resulting in a deposit metal having excellent properties. In order to attain such a result, as seen from FIG. I, it is necessary that the Al-Mg alloy includes K and KCl and NaCl in the amount of at least 0.006 percent by weight of the Al-Mg alloy. However, if these chlorides are included in a substantial amount in the Al-Mg alloy, the amount of moisture to be absorbed into a deposit metal will increase as seen in FIG. 2. Accordingly, it is necessary not to use these ingredients in excess of the upper limit of the specified amount range or 0.06 percent. The most preferable amount range of these ingredients is 0.006--0.025 percent and in such a case K and Na are preferably used in the ratio of about one to one by weight. And K and Na are preferably employed in the form of carbonates thereof because the addition of these ingredients in their elemental forms to the other ingredients of the Al-Mg alloy is technically difficult and similarly, the addition of these ingredients in their compound forms to the other ingredients of the Al-Mg alloy is also not advisable. When the Al-Mg alloy having the above composition is blended with the other powdery ingredients of the flux of the wire electrode, for the purpose of the present invention, it is necessary that the alloy is used in the amount range 2-5 percent by weight of the total composite wire electrode.- T he use of the Al-Mg alloy below the lower limit of the prescribed amount range will not exhibit its function as the denitrification agent. On the other hand, the use of the alloy in excess of the upper limit of the prescribed amount range will result in lowering of the ductility of a formed deposit metal. And the use of the Al-Mg alloy in any amount deviating from the prescribed amount range will not attain the purpose to which the present invention is directed.

The following Table 1 shows the results of various welding operations conducted on workpieces using wire electrodesdncluding various Al-Mg alloys which contain Na and K in varying amounts according to the present invention and conventional wire electrodes, respectively and all the welding operations were conducted by the open-arc automatic welding be too high to form a satisfactory bead shape and air voids will develop in the deposit metal as well as increasement of the amount of intervenient substances therein. On the other hand. the amount of Cal exceeds 1 1 percent by weight of the total process. The ompositions of the elding fluxes in the ire 5 wire. that is, the upper limit of the amount range prescribed electrodes and welding conditions employed in these operafor the ingredient. the viscosity of slag formed will be too low lions were follOWSI to cause the slag to envelope the deposit metal resulting in un- COMPOSITION ()F wELDlNG FLUX satisfactory workability. The Mn contained in the novel wire electrode flux serves as a conventional deoxidization agent (Excluding Al'Mg Alloy) and the amount of the Mn usually must vary depending upon 10% the strength required for a structure to be welded in order to Fe Mr cause the amount of the ingredient to conform with the (70% Mn) 06% required strength of the structure. in the novel wire electrode,

Ni 1% the amount of Mn employed is preferable and practicable within the range O.l-l.5 percent by weight of the total wire BY EIG 0} H TOTAL w ELECTRQDE electrode. The Ni employed in the novel wire electrode flux serves as the so-called austenite former and as the amount of powder 48% Al which is the ferrite former increases, the austenite former Sloz 0 l% reduces the size of the crystal particles of a deposit metal so as In any of the wlre electrodes employeq' total to increase the strength and stabilize the impact value of the the Powdery flux was 21 Percent by weght of the total wlre deposit metal. Although the amount of Ni to be employed in electrode the novel wire electrode flux may vary depending upon the WELDING CONDITIONS amount of the Al-Mg alloy employed in the wire flux, when 25 the Al-Mg alloy is employed in the amount range 25 percent 400 Amp 27 v. (AC) 4 layer finish by weight of the total wire electrode the Ni is preferably emworkpieces Mild steel plates 19 mm. thick) with ployed in the amount range 0.8-2 percent by weight of the V-shaped grooves of 50 angle total wire. if the amount of the Ni to be employed in the wire TABLE 1 Amount of Blending Amount of Amount of NaClKCl in amount of Al absorbed N absorbed Al-Mg Al-Mg in de osit in deposit; X-ray alloy, by alloy, by meta by metal, b J IS Impact weight percent weight percent weight percent weight percent grade value Wire Number:

Norm-Nos. 3-6 were the novel composite wire electrodes.

As seen from the above Table l, when welding operations flux is less than 0.8 percent. that is, the lower limit described were conducted using composite wire electrodes including Alfor the ingredient, the anticrack property of a deposit metal Mg alloys which contain neither Na nor K (Nos. 1 and 2 wire formed will be low. electrodes), it was found that formed deposit metals had grave In addition to the above-mentioned ingredients, the novel defects with respect to X-ray properties and impact value and wire electrode flux sometimes may contain elements such as the deposit metals were not practically useful. On the contra- Al Zr and Ti or alloys thereof as the auxiliary denitrification ry, when welding operations were conducted using novel comagents, elements such as Si, Cr, Mo, B, V, W, C and Cu or alposite wire electrodes, it was confirmed that deposit metals loys thereof as alloying ingredients and TiO- SiO M 0 having excellent properties could be formed. Deposit metals ZrO MgO, MnO, MnO K20, Na20, CaCO MgCO and obtained by the use of Nos. 7 and 8 wire electrodes had ab- BaCO as auxiliary slag forming agents and/or Fe as melting sorbed substantial amounts of moisture and low X-ray properaccelerating metal. ties. M According to the present invention, it is necessary that the And the reason for which the use of CaF Mn and Ni in adamount of the powdery flux in the composite wire electrode dition to Al-Mg alloy in the novel composite wire electrode be maintained within the range 10-40 percent by weight of are as follows: the total wire electrode and the total amount of CaFZ-Mn-Ni- As fluorides. although there are a great variety of sub- Al.Mg which are essential ingredients of the novel wire elecstances other than CaF CaF is preferably over other trode flux be at least 55 percent by weight of the total wire fluorides because the CaF when used in the novel wire clecelectrode as 100 percent. Accordingly, the novel wire electrode improves the fluidity and workability of slag and espetrode flux may comprise only these four essential ingredients, cially accelerates the enveloping action and removal of slag. but in addition to these four ingredients, when the wire elec- The amount of CaF to be blended with the other ingredients trode flux further contains the above-mentioned auxiliary inof the flux of in the novel wire electrode may vary depending gredients the total amount of the auxiliary ingredients must be upon the amount of the Al-Mg contained in the wire flux, less than (l0055) percent by weight of the total wire elecwhen the wire flux contains the Al-Mg alloy in the amount of trode. And the amount of the auxiliary denitrification agent 2-5 percent by weight of the total wire. CaF may be cmingredients which are added to the primary denitrification ployed in the amount of 6-1 1 percent by weight of the total agent ingredients must be less than 1 percent by weight of the wire. lf the amount of the CaF is less than 6 percent by weight total wire electrode, the amount of the alloying elements must of the total wire, that is, the lower limit of the amount range be less than l percent by weight of the total wire electrode, the

prescribed for the ingredient, the viscosity of slag formed will amount of the auxiliary slag forming agent ingredients must be less than 2 percent by weight 6? the total wire electrode and finally the amount of iron powder must be less than 18 percent by weight of the total wire electrode.

On the other hand, the metal sheath of the composite wire electrode may be formed by either carbon steel or low carbon steel as desired and the composition of the metal sheath is not limited to any specific one. However, usually the metal sheath is formed by shaping a hooped blank into a tubular shape and therefore, the metal sheath is preferably made from an easily processible material such as mild steei. The shape of the metal sheath of the composite wire electrode is not limited to a simple pipe shape, but may be of any other more complicated cross section configuration such as that having inwardly and radially extending fins, for example.

The following is the most pertinent examples of this invention.

EXAMPLE 1 Composition of wire:

A wire electrode, 3.2 mm. in diameter made of 0.2 X 23 mm. mild steel hoop containing 0.03 percent of C, 0.35 percent of Mn and 0.01 percent of Si, which includes fluxes of the following amounts by weight of the total Tensile strength 52 KgJmm. Impact value 16.5 Kg. m.

EXAMPLE 2 Composition of wire:

A wire electrode, 3.2 mm. in diameter, made of mild steel identical to that of Example 1, which includes fluxes of the following amounts by weight of the total wire.

CaF 8 wt% Fe-Mn 1 wt% (Mn 70 percent) Al-Mg 3.5 wt% (Al 40% chloride 0.02%) Ni 1 wt% Fe (powder) 6 wt% Welding conditions:

workpieces Mild steel plates (25mm. thick) 380 Amp. 25 v. Buttwelding Result:

X-Ray property no defect Tensile strength 51 KgJmm. Bending test good Impact value Kg. m.

EXAMPLE 3 Composition of wire:

A wire electrode, 3.2 mm. in diameter, made of mild steel identical to that of Example 1, which includes fluxes of the following amounts by weight of the total wire.

CaF 7 wt% Mn 0.3 wt% Al-Mg 2.5 wt% (Al 60% chloride 0.03%)

Ni 1 wt% Fe(powder) ll wt% Welding conditions:

workpieces Mild steel plates 19mm. thick) 400A. 27 V. Buttwelding Results:

X-Ray property no defect Tensile strength 54 Kg/mm. lmpact value 18 Kg. m.

EXAMPLE 4 Composition of wire:

A wire electrode, 2.4 in diameter, made of 0.2 X17 mm. mild steel hoop containing 0.04 percent of C, 0.37 percent of Mn and 0.01 percent of Si, which includes fluxes of the following amounts by weight of the total wire.

CaF 12 wt% Fe-Mn 0.5 wt% (Mn 70 percent) Al-Mg 3 wt% (Al 50% chloride 0.02%) Ni 1 wt% CaO 1.5 wt% Fe (powder) 4 wt% Welding conditions:

Workpieces Mild steel.plates( 16mm. thick) 400 Amp. 26 V. Horizontal fillet welding Results:

Work efficiency excellent Outline of bead excellent Structure no defect From the foregoing, it will be understood that since the novel composite wire electrode flux contains the above-mentioned specific Al-Mg alloy blended therein in the above-mentioned specific Al-Mg alloy blended therein in the abovedescribed amount range, the amount of N to be contained in a deposit metal can be made less than that in a deposit metal formed by any convention composite wire electrode and in addition, the total amount of the denitrification agent to be contained in the wire electrode flux can be made less than that in a deposit metal formed by any conventional wire electrode whereby the ductility in the notch in a deposite metal can be significantly improved over that obtainable by any conventional wire electrode. Thus, the novel composite wire effectively eliminates the. defects experienced with the use of the conventional open-type automatic submerged arc-welding composite wire electrodes and has a great industrial value.

Although the best mode contemplated for carrying out the present invention has been herein shown and described, it will be apparent to those skilled in the art that modification and variation may be made without departing from what is regarded to be the subject matter of the invention as set-forth in the appended claims.

We claim:

I. A composite wire electrode for use in open-type arcwelding of steel without shielding gas, comprising a metal sheath and a powdery flux filled in said sheath, said flux essentially comprising by weight of the total wire electrode, respectively 6-l4 percent of CaF 0.ll.5 percent of Mn, 0.8-2 percent of Ni and 2-5 percent of Al-Mg alloy containing NaCl and KCI in the total amount of 0.006-0.06 percent by weight of the Al-Mg alloy.

2. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising one or more members selected from the group comprising Ti, Zr and the like as denitrification element or elements.

3. A composite wireelectrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising one or more members selected from the group comprising Si, Cr, Co, B, V, W, C, Cu as alloying element or elements.

4. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising one or more members selected from the group comprising TiO SiO A1 0 ZrO MgO, CaO, MnO, MnO,, K Na CaCo MgCO and BaCO 5. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim I, said powdery flux further comprising Fe powder in the amount of 2 l 8 percent by weight of the total wire electrode as one ingredient of the flux composition of said wire electrode.

6. A composite wire electrode for use in open-type arcwelding of steel without shielding gas as set forth in claim I,

said powdery flux in said metal sheath being in the amount of -40 percent by weight of the total wire electrode and in said Al-Mg alloy Al is 35-65 percent and Mg is 56-35 per- 

1. A composite wire electrode for use in open-type arc-welding of steel without shielding gas, comprising a metal sheath and a powdery flux filled in said sheath, said flux essentially comprising by weight of the total wire electrode, respectively 614 percent of CaF2, 0.1- 1.5 percent of Mn, 0.8- 2 percent of Ni and 2- 5 percent of Al-Mg alloy containing NaCl and KCl in the total amount of 0.006- 0.06 percent by weight of the Al-Mg alloy.
 2. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising one or more members selected from the group comprising Ti, Zr and the like as denitrification element or elements.
 3. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising one or more members selected from the group comprising Si, Cr, Co, B, V, W, C, Cu as alloying element or elements.
 4. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising one or more members selected from the group comprising TiO2, SiO2, Al2O3, ZrO2, MgO, CaO, MnO, MnO2, K20, Na20, CaCo3, MgCO3 and BaCO3.
 5. A composite wire electrode for use in arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux further comprising Fe powder in the amount of 2- 18 percent by weight of the total wire electrode as one ingredient of the flux composition of said wire electrode.
 6. A composite wire electrode for use in open-type arc-welding of steel without shielding gas as set forth in claim 1, said powdery flux in said metal sheath being in the amount of 10- 40 percent by weight of the total wire electrode and in said Al-Mg alloy Al is 35- 65 percent and Mg is 56- 35 percent by weight of the total wire electrode and the total amount of contained in said Al-Mg alloy is 0.006- 0.025 percent by weight of said Al-Mg alloy. 